| Standard Grade |
| The oxygen barrier properties of
Soarnol depend on ethylene content and humidity.
The most suitable grade for a given purpose can
be determined according to application and manufacturing
process. |
 |
|
|
|
555 |
|
D2908 |
DT2903 |
DC3212 |
DC3203F |
E3808 |
ET3803 |
A4412 |
AT4403 |
H4815 |
Ethylene
content |
mol% |
29 |
32 |
38 |
44 |
48 |
Density |
g/cm3 |
1.21 |
1.19 |
1.17 |
1.14 |
|
Melting
point *1 |
deg C |
188 |
183 |
173 |
164 |
158 |
Crystallization temp.
*1 |
deg C |
163 |
160 |
152 |
144 |
138 |
Glass
transition temp. *1 |
deg C |
62 |
61 |
58 |
55 |
48 |
MFR
*2 |
g
/10min |
8 |
3.2 |
12 |
3.2 |
8 |
3.2 |
12 |
3.5 |
16 |
Apparent
melt viscosity *3 |
210degC
poise |
9000 |
24000 |
5500 |
24000 |
9000 |
24000 |
5500 |
20000 |
|
210degC
Pa.s |
900 |
2400 |
550 |
2400 |
900 |
2400 |
550 |
2000 |
|
230degC
poise |
5000 |
13000 |
2500 |
13000 |
5000 |
12000 |
2500 |
10000 |
|
230degC
Pa.s |
500 |
1300 |
250 |
1300 |
500 |
1200 |
250 |
1000 |
|
OTR *4 |
cc.20µm
/m2.day.atm |
0.4 |
0.5 |
0.7 |
1.5 |
2.8 *5 |
cm3.20
µm/m2.
24hrs.MPa |
4 |
5 |
7 |
15 |
28 *5 |
Manufacturing
process |
Blown
film |
|
o |
|
o |
|
o |
|
o |
|
Cast
film |
o |
|
o |
|
o |
|
o |
|
o |
| Sheet |
|
o |
|
o |
|
o |
|
o |
|
| Bottle |
o |
o |
|
o |
|
|
|
|
|
| Pipe |
o |
|
o |
o |
|
|
o |
|
o |
|
•
1 |
Measured
with DSC. |
•
2 |
210deg C(410deg
F), 230deg C(446deg F) |
•
3 |
Measured with
melt flow tester which has 1mm *10mmL nozzle and 490N{50kgf}load. |
•
4 |
20deg C*65%RH
The data in the table are in house standards and
not guaranteed values. |
•
5 |
23deg C*70%RH |
|
| Special Grade etc. |
• |
Thermoforming
grades for PE, PSt or PP construction |
• |
Flex-crack
resistance grades |
• |
Purging
resin for EVOH |
• |
Regrind
agent for (PE,PSt or PP/EVOH) system |
• |
If you
want to try to use above special grades, pleasecontact us. |
|
|
|
|